|Year : 2016 | Volume
| Issue : 3 | Page : 253-258
Osteogenic potential of laser modified and conditioned titanium zirconium surfaces
P David Charles1, Ponsekar Abraham Anandapandian2, Shila Samuel3
1 Department of Prosthodontics, SRM Dental College, Chennai, Tamil Nadu, India
2 Department of Prosthodontics, Shree Balaji Dental College, Chennai, Tamil Nadu, India
3 Department of Biochemistry, VRR Institute of Biomedical Science, Chennai, Tamil Nadu, India
|Date of Submission||23-Mar-2016|
|Date of Acceptance||23-May-2016|
|Date of Web Publication||18-Jul-2016|
P David Charles
29/17, Secretariat Colony, 1st Street, Kilpauk, Chennai - 600 010, Tamil Nadu
Source of Support: None, Conflict of Interest: None
Statement of Problem: The osseointegration of dental implant is related to their composition and surface treatment. Titanium zirconium (TiZr) has been introduced as an alternative to the commercially pure titanium and its alloys as dental implant material, which is attributed to its superior mechanical and biological properties. Surface treatments of TiZr have been introduced to enhance their osseointegration ability; however, reliable, easy to use surface modification technique has not been established. Purpose: The purpose of this study was to evaluate and compare the effect of neodymium-doped yttrium aluminum garnet (Nd-YAG) laser surface treatment of TiZr implant alloy on their osteogenic potential. Materials and Methods: Twenty disc-shaped samples of 5 mm diameter and 2 mm height were milled from the TiZr alloy ingot. The polished discs were ultrasonically cleaned in distilled water. Ten samples each were randomly selected as Group A control samples and Group B consisted of Nd-YAG laser surface etched and conditioned test samples. These were evaluated for cellular response. Cellular adhesion and proliferation were quantified, and the results were statistically analyzed using nonparametric analysis. Cellular morphology was observed using electron and epiflurosence microscopy. Results: Nd-YAG laser surface modified and conditioned TiZr samples increased the osteogenic potential. Conclusion: Nd-YAG laser surface modification of TiZr, improves the cellular activity, surface roughness, and wettability, thereby increasing the osteogenic potential.
Keywords: Cell culture, neodymium-doped yttrium aluminum garnet laser modification, osteogenesis, titanium zirconium
|How to cite this article:|
Charles P D, Anandapandian PA, Samuel S. Osteogenic potential of laser modified and conditioned titanium zirconium surfaces. J Indian Prosthodont Soc 2016;16:253-8
|How to cite this URL:|
Charles P D, Anandapandian PA, Samuel S. Osteogenic potential of laser modified and conditioned titanium zirconium surfaces. J Indian Prosthodont Soc [serial online] 2016 [cited 2021 May 13];16:253-8. Available from: https://www.j-ips.org/text.asp?2016/16/3/253/186403
| Introduction|| |
Commercially pure titanium (cpTi) has been the material of choice for dental implants due to their inert property to osseointegrate. However, the mechanical properties of cpTi proved to be insufficient. These properties are to be considered while the edentulous ridge is narrow and only small diameter implants of ≤3.5 mm could be used.,,, The use of a small diameter implant is prone to increased chances of fatigue fracture.,,,, Hence, it was necessary to develop an implant material which improved the mechanical strength while retaining the necessary biological qualities of existing titanium alloys. The biocompatibility and the mechanical strength of titanium zirconium (TiZr)-based alloys proved to be better in comparison with cpTi. The binary TiZr alloy has increased mechanical stability with respect to elongation and fatigue strength. In addition, the corrosion resistance of TiZr is better and improved than cpTi. The α-phase crystal structure of TiZr alloy ensures that the surface treatments that have been successful on Ti implants can still be implemented on it. Further, the strength of TiZr implant is found to be greater than the strength of cold-worked, Grade IV Ti, which makes it a great candidate for small diameter implants, even in high loading situations.
When considering the mechanical properties, the biological property of the alloy should also be equally evaluated so that it has no negative influence on the desired mechanism. Many metals are known to strongly inhibit growth of osteoblasts (e.g., vanadium [V], niobium [Nb]) whereas Ti and Zr have not shown to inhibit osteogenesis with preferred osseointegration capabilities.
The osseointegration capability of an implant depends not only on the type of implant material but also to do with type of surface topography that aids in enhancing an excellent contact with the bone. Key events of biological activity such as early fibrin clot formation, platelet activation, creating a three-dimensional (3D) environment that supports bone formation, increased production of bone-related growth factors, and reduced osteoclastic activity are achieved by the micro-topography of dental implant surfaces. It is reported in the literature that there is an increased synthesis of extracellular matrix with subsequent mineralization on the rougher surfaces. However, many studies did not accept to the cell response mechanism in dental implants. Thus, there is no agreement about the importance of the degree of roughness (Ra) and its relationship to surface wettability, adhesion, and cellular proliferation.,,,
Lasers have been reported to create 3D complex surface irregularities in a nanoscale level with no contamination. There is no report in the literature on modifying the laser-treated surface by inducing the hydrophilic property., The aim of the study was to evaluate the surface characteristics, Ra, and wettability of TiZr implant alloy samples following surface modification using neodymium-doped yttrium aluminum garnet (Nd-YAG) laser and the Osteoblastic cell response.
| Materials and Methods|| |
For the purpose of the study, the TiZr implant alloy samples were separated into two separate groups as Group A and Group B. Group A was untreated and kept as control group whereas Group B samples were laser modified and subjected to evaluation of surface Ra and evaluation of surface wettability. Following the surface analysis, the same samples were subjected to evaluation of cells adhesion, evaluation of cell proliferation, and mineralized bone-like nodule formation. Finally, the results were obtained microscopically statistically.
Preparation of samples
Disc samples of 2 mm thickness and 5 mm diameter were milled from TiZr ingot. These discs were subjected to silicon carbide abrasive polishing and rinsed with distilled water, later autoclaved, and air-dried. The samples were randomly grouped as A and B of 10 samples each. Group A (n = 10) polished untreated samples were used as control [Figure 1] and Group B (n = 10) were surface treated with Nd-YAG laser [Figure 2].
|Figure 2: Laser surface-modified and conditioned titanium zirconium samples|
Click here to view
Laser surface modification
Group B (n = 10) samples were subjected to laser surface modification using Nd: YAG laser (Fotona Fidelis plus III, Slovenia). The glass fiber of the Nd: YAG laser was moved over the samples in a linear motion with 8 W power, 300 mJ/pulse energy, and 50-kHz pulse frequency with 1064 nm wavelength. Following surface treatment, all specimens were subjected to cleaning with water steam spray and ultrasonic cleaning using distilled water for 10 min at 80°C, and then rinsed in distilled water. The excess water was removed by air syringe at room temperature, and all specimens were air dried, followed by conditioning with 78–85% nitrogen gas and stored in 0.9% NaCl solution to maintain the clean oxide layer with its hydrophilic properties.
The uniformity in surface irregularities was assessed using scanning electron microscope (SEM) and epifluorescence microscope (alizarin red [AR] stain) (Olympus BX51) [Figure 3]a and [Figure 3]b. The microstructural analysis of surface-modified samples was performed with an SEM (Carl Zeiss Pvt., Ltd., UK., EVO MA 15, magnification range ×20–200,000).
|Figure 3: (a) Scanning electron microscope view of polished titanium zirconium surface. (b) Scanning electron microscope view of laser-modified and conditioned titanium zirconium surfaces|
Click here to view
Evaluation of surface roughness
Roughness (Ra) was measured using a Surtronic 3 (Taylor Hobson) profilometer with a cutoff of 0.25 mm from three different directions 120° apart. The mean of two sets of values was reported as Ra value of the tested samples.
Evaluation of surface wettability
Following the surface treatment, five samples from each experimental group were subjected for wettability testing. An adjustable volume digital micropipette (sigma), positioned perpendicular, was used to deposit 0.25 ml of saline solution onto the surface of the samples. For standardization of the values, the angle changes were monitored at 1 s, 30 s, and 60 s.
Evaluation of cells adhesion
Following gamma sterilization, the samples of both groups were plated with commercially available human calvarial osteoblastic cells (Grace Scientific co.) with a cell density of 1 × 104 cells/cm 2 per well on a 24-well plate. Ten discs from each experimental group were used and three samples were randomly selected from each group for cell morphology analysis.
Evaluation of cell proliferation
Cell proliferation was evaluated by determining the number of cells that adhered onto the samples at 24 h, 48 h, and 72 h after plating in triplicate. Twenty wells were counted and the number of viable cells collected was obtained using a hemocytometer and the trypan blue exclusion test.
The total numbers of cells were calculated as total counted number of cells × dilution × 104/number of hemocytometers. Following which the viable cell population was found by dividing the number of viable cells and multiplying the result by hundred.
Mineralized bone-like nodule formation
One sample from each experimental group was fixed using 4% formaldehyde in phosphate buffer, pH 7, for 2 h at room temperature. Postfixation was accomplished with 1% osmium tetroxide with the same buffer. The samples were then dehydrated using a graded series of ethanols, immersed in hexamethyldisilazane for 30 min and air dried. Following which the samples were stained with 2% AR (sigma), pH 4.2, for 8 min at room temperature. The stained areas (AR) were evaluated by epifluorescence microscope (Olympus BX51). The percentage of cells occupied by AR-stained nodules was determined using image tool software (Image-Pro plus AMS).
The existence of significant differences between the surface-modified samples was identified using a nonparametric analysis which calculated the averages of ranks and quartiles. Data were analyzed by Student's t-test. All values were compared for their significance at a range of P < 0.05.
| Results|| |
The mean Ra of polished samples (control group) in comparison with the laser-treated and modified samples (test group) were lower [Table 1]. However, the ten polished samples had an average value of 0.03–0.09 µm, with an acceptable value for a mechanically polished sample (P = 0.01) suggesting that the laser modification has a positive effect on altering the structure of the TiZr.
|Table 1: Evaluated surface parameters on the experimental and control discs|
Click here to view
There was a low level of contact angle obtained on the samples treated with modified laser treatment, and this surface was characterized by more of hydrophilic and polar behavior in comparison with the control group [Table 1]. The rate of dispersion was found to be low for both the samples.
The human calvarial osteoblastic cells responded differently, depending on the chemical composition and the surface topography of the exposed surfaces [Table 1]. There was a significant difference in level of adhesion of cells on the surface-treated samples after 24 h. There was even more pronounced adhesion of cells onto the laser modified surface.
There was a similarity in cellular behavior for both cell proliferation and cell adhesion. There were no statistically significant differences between the control and the modified laser samples at the end of 24 h, but there was a significant difference in cell proliferation on modified laser samples at the end of 72 h [Table 1].
There was a variation in the morphology of Osteoblastic cells according to the surface pattern. Due to the low Ra on the polished samples, the cells were found to be with scattered contact regions between them and failed to follow an orientation parallel to polishing lines. There were many focal adhesion areas present on the modified laser-treated surface with dendritic projections and filopodia resulting from the 3D rough surfaces and also the cells were found to be very close to one another.
The AR staining is usually done to confirm the osteoblastic cell adhesion. Depending on the intensity of the AR-stained positive areas, the samples were qualitatively assed under epifluorescence microscope. Microscopic inspection revealed more dotted reddish areas on laser-treated discs than polished samples which lacked uniformity in cell adhesion [Figure 4]a and [Figure 4]b. Qualitative analysis of this study showed increased amount of AR-stained regions with uniform distribution of cells forming mineralized nodules on modified laser discs with 95% density in comparison with polished samples with a grading of 40% density on both epifluorescence and Scanning electron microscopic evaluation [Figure 5]a and [Figure 5]b.
|Figure 4: (a) Epifluorescence microscopic view of cells adhering onto polished titanium zirconium surfaces. (b) Epifluorescence microscopic view of cells adhering onto laser-modified and conditioned titanium zirconium surfaces|
Click here to view
|Figure 5: (a) Scanning electron microscope view of mineralized bone-like nodules onto polished titanium zirconium surfaces. (b) Scanning electron microscope view of mineralized bone-like nodules onto laser-modified and conditioned titanium zirconium surfaces|
Click here to view
| Discussion|| |
Topographical surface alterations of titanium and its alloys on a particular scale proved to enhance the osseointegration capability of the dental implant. This was achieved because of the surface Ra, changes in chemical composition and surface free energy., However, the mechanical properties of cpTi prove to be insufficient in many situations.,,, The risk in using a small diameter implant is the increase chances of fatigue fracture.,,,, Hence, it was more important to develop a small diameter implant material which can improve the mechanical strength as well retains the necessary qualities of existing titanium alloys.
The biocompatibility and the mechanical strength of TiZr-based alloys proved to be better in comparison with cpTi. Hence, this study was focused on modification of TiZr implant alloy surface with a laser source. The laser source of choice was Nd: YAG as it can create 3D structure at micrometer and nanometer level on the implant surfaces whereas other lasers can only be used for decontamination of implant surface. This technique is more supportive in creating complex surface geometries. In this method, short pulse of light is focused on a single spot and moved in a linear motion with generation of heat without altering the nature of the metal. Hence, the technique can be done quicker with contamination free complex microstructures with high resolution. These factors have made the technique interesting for fabricating a geometrically complex biomedical implant surface. To achieve an enhanced hydrophilic surface, the Nd-YAG laser-modified samples were also rinsed in nitrogen atmosphere and stored in saline solution to aid in reducing the amount of carbon contamination and for improving the hydrophilicity.
The surface Ra was analyzed using contact profilometry which has its scale resolution is in microns. Even then the Ra values of polished TiZr samples and Nd-YAG modified samples had significant differences.
The surface with highest Ra value (Ra - 0.18 µm) showed the lowest liquid-titanium contact angles. This result is related to Ra of the surface and the regularity of the formed pattern, both of which reduced the possibility of retaining any contaminants in the micro deformations of the modified surface. Previous studies on surface characteristics feature the way osteoblasts adhere to and proliferate on titanium mostly to wettability , and adding on to it hydrophilic surfaces proved better conditions for cell adhesion in comparison with hydrophobic surfaces. Nevertheless, a close relationship is observed between TiZr Ra and wettability and in the present study, the surface modification by laser followed by conditioning showed a reduction in contact angle. This confirms that a surface containing better wettability will exhibit better cell adhesion. Thus, laser etching and conditioning proved to be an effective technique for modifying a TiZr implant alloy surface in terms of increased Ra and increased wettability.
In vitro analysis using cell culture is usually done to evaluate the potential for osseointegration of biomaterials as stated the models used in this study create a well-controlled and accessible micro environment for providing a consistent data for analysis , and also provided a better understanding of the early stages of osseointegration and various cell interaction onto the modified surfaces.
In a controlled osteogenic environment, there is an uninterrupted clonal expansion of osteoprogenitors followed by their entry into the osteoblast differentiation sequence.,,, The osteoprogenitors are the ones which are responsible for the bone formation rate, replication rate, and they determine the lifespan and number of active osteoblast., These osteoprogenitors play an important role in stimulation of osteoblastic activity and mineralized bone matrix formation on treated or modified implant surfaces.
Surface wettability plays an important role in enhancing the osteogenic activity on surface modified metals. Protein adsorption, cell adhesion, cell distribution, and enhanced osteoblastic activity can get altered if there is a change in surface wettability and surface energy.,,, Hence, to achieve surface wettability, it is necessary for the implant surface to be hydrophilic to induces rapid osseointegration.,
In the present study, Group B samples were subjected to hydrophilic treatment following a laser surface modification. The surface topography of modified laser-treated samples revealed nanopits of 24 ± 5 nm in diameter which can influence the immediate and equilibrium contact angles to decrease and thereby converting the hydrophobic surface into an extremely hydrophilic surface. This increased the rate of mineralized bone matrix formation on the laser-treated surfaces.
Considering the above factors, it was found that surface modification with modified Nd-YAG laser on TiZr implant alloy showed increased mineralized bone-like nodule formation with uniformity in comparison with polished nontreated samples. This is similar to the results of the studies conducted on CpTi using the laser sources., A limitation of the present study is that the results were based on the laboratory findings and yet to be confirmed with the clinical study.
| Conclusion|| |
Within the limitation of this study, the following conclusion was made. Nd-YAG laser surface treatment on TiZr had positive effects on the early cellular events leading to cell adhesion and proliferation. Surface wettability was greater in the test group while maintaining biocompatibility characteristics.
Financial support and sponsorship
Conflicts of interest
There are no conflicts of interest.
| References|| |
Vannoort R. Titanium – The implant material of today. J Mater Sci 1987;22:3801-11.
Steinemann SG. Titanium – The material of choice? Periodontol 2000 1998;17:7-21.
Al-Nawas B, Brägger U, Meijer HJ, Naert I, Persson R, Perucchi A, et al.
A double-blind randomized controlled trial (RCT) of titanium-13zirconium versus titanium grade IV small-diameter bone level implants in edentulous mandibles – Results from a 1-year observation period. Clin Implant Dent Relat Res 2012;14:896-904.
Romeo E, Lops D, Amorfini L, Chiapasco M, Ghisolfi M, Vogel G. Clinical and radiographic evaluation of small-diameter (3.3-mm) implants followed for 1-7 years: A longitudinal study. Clin Oral Implants Res 2006;17:139-48.
Zinsli B, Sägesser T, Mericske E, Mericske-Stern R. Clinical evaluation of small-diameter ITI implants: A prospective study. Int J Oral Maxillofac Implants 2004;19:92-9.
Allum SR, Tomlinson RA, Joshi R. The impact of loads on standard diameter, small diameter and mini implants: A comparative laboratory study. Clin Oral Implants Res 2008;19:553-9.
Schwarz MS. Mechanical complications of dental implants. Clin Oral Implants Res 2000;11 Suppl 1:156-8.
Parr GR, Gardner LK, Toth RW. Titanium: The mystery metal of implant dentistry. Dental materials aspects. J Prosthet Dent 1985;54:410-4.
Naganawa T, Ishihara Y, Iwata T, Koide M, Ohguchi M, Ohguchi Y, et al. In vitro
biocompatibility of a new titanium-29niobium-13tantalum-4.6zirconium alloy with osteoblast-like MG63 cells. J Periodontol 2004;75:1701-7.
Grandin HM, Berner S, Dard M. Review of titanium zirconium (TiZr) alloys for use in endosseous dental implants. Materials2012;5:1348-60.
Ikarashi Y, Toyoda K, Kobayashi E, Doi H, Yoneyama T, Hamanaka H, et al
. Improved biocompatibility of titanium-zirconium (Ti-Zr) alloy: Tissue reaction and sensitization to Ti-Zr alloy compared with pure Ti and Zr in rat implantation study. Mater Trans 2005;46:2260-7.
Kawai H, Shibata Y, Miyazaki T. Glow discharge plasma pretreatment enhances osteoclast differentiation and survival on titanium plates. Biomaterials 2004;25:1805-11.
Lampin M, Warocquier-Clerout R, Legris C, Degrange M, Sigot-Luizard MF. Correlation between substratum roughness and wettability, cell adhesion and cell migration. Biomaterials 1977;36:99-108.
Ponsonnet L, Reybier K, Jaffrezic N, comte V, Lagneau C, Lissac M. Relationship between surface properties (roughness, wettability) of titanium and titanium alloys and cellbehavior. Mater Sci Eng 2003;C23:551-60.
Hanks CT, Wataha JC, Sun Z.In vitro
models of biocompatibility: A review. Dent Mater 1996;12:186-93.
Brunette DM. In vitro
models of biological responses to implants. Adv Dent Res 1999;13:35-7.
Marticorena M, Corti1 G, Olmedo D, Guglielmotti MB, Duhalde S. Laser surface modification of Ti implants to improve osseointegration. J Phys Conf Ser 2007;59:662-5.
Faeda RS, Tavares HS, Sartori R, Guastaldi AC, Marcantonio E Jr. Evaluation of titanium implants with surface modification by laser beam. Biomechanical study in rabbit tibias. Braz Oral Res 2009;23:137-43.
Czyrska-Filemonowicz A, Buffat PA, Luck M, Moskalewicz T, Rakowski W, Light J, et al
. Transmission electron microscopy and atomic force microscopy characterization of titanium – Base alloys nitride under glow discharge. Acta Mater 2005;53:4367-77.
Gaggl A, Schultes G, Müller WD, Kärcher H. Scanning electron microscopical analysis of laser-treated titanium implant surfaces – A comparative study. Biomaterials 2000;21:1067-73.
Chang EJ, Kim HH, Huh JE, Kim IA, Seung Ko J, Chung CP, et al.
Low proliferation and high apoptosis of osteoblastic cells on hydrophobic surface are associated with defective Ras signaling. Exp Cell Res 2005;303:197-206.
Nanci A, Zalzal S, Gotoh Y, McKee MD. Ultrastructural characterization and immunolocalization of osteopontin in rat calvarial osteoblast primary cultures. Microsc Res Tech 1996;33:214-31.
Bellows CG, Aubin JE, Heersche JN, Antosz ME. Mineralized bone nodules formed in vitro
from enzymatically released rat calvaria cell populations. Calcif Tissue Int 1986;38:143-54.
Bellows CG, Aubin JE. Determination of numbers of osteoprogenitors present in isolated fetal rat calvaria cells in vitro
. Dev Biol 1989;133:8-13.
Stein GS, Lian JB. Molecular mechanisms mediating proliferation/differentiation interrelationships during progressive development of the osteoblast phenotype. Endocr Rev 1993;14:424-42.
Jilka RL, Weinstein RS, Bellido T, Parfitt AM, Manolagas SC. Osteoblast programmed cell death (apoptosis): Modulation by growth factors and cytokines. J Bone Miner Res 1998;13:793-802.
Jilka RL, Weinstein RS, Bellido T, Roberson P, Parfitt AM, Manolagas SC. Increased bone formation by prevention of osteoblast apoptosis with parathyroid hormone. J Clin Invest 1999;104:439-46.
De Oliveira PT, Rosa AL, Zalzal S, Richert L, Yi JH, Wuest J, et al
. Controlled chemical oxidation of titanium creates a nanotopography that enhances in vitro
osteogenesis. J Biomed Mater Res A 2007;80:554-64.
Roach P, Farrar D, Perry CC. Interpretation of protein adsorption: Surface-induced conformational changes. J Am Chem Soc 2005;127:8168-73.
Lim JY, Hansen JC, Siedlecki CA, Hengstebeck RW, Cheng J, Winograd N, et al.
Osteoblast adhesion on poly(L-lactic acid)/polystyrene demixed thin film blends: Effect of nanotopography, surface chemistry, and wettability. Biomacromolecules 2005;6:3319-27.
Webb K, Hlady V, Tresco PA. Relative importance of surface wettability and charged functional groups on NIH 3T3 fibroblast attachment, spreading, and cytoskeletal organization. J Biomed Mater Res 1998;41:422-30.
Faucheux N, Schweiss R, Lützow K, Werner C, Groth T. Self-assembled monolayers with different terminating groups as model substrates for cell adhesion studies. Biomaterials 2004;25:2721-30.
Zhao G, Schwartz Z, Wieland M, Rupp F, Geis-Gerstorfer J, Cochran DL, et al.
High surface energy enhances cell response to titanium substrate microstructure. J Biomed Mater Res A 2005;74:49-58.
Rupp F, Scheideler L, Olshanska N, de Wild M, Wieland M, Geis-Gerstorfer J. Enhancing surface free energy and hydrophilicity through chemical modification of microstructuredti-tanium implant surfaces. J Biomed Mater Res A 2006;76:323-4.
[Figure 1], [Figure 2], [Figure 3], [Figure 4], [Figure 5]