Year : 2020  |  Volume : 20  |  Issue : 4  |  Page : 363-370

Effect of post etching cleansing on surface microstructure, surface topography, and microshear bond strength of lithium disilicate

Department of Prosthodontics, Manipal College of Dental Sciences, Manipal Academy of Higher Education, Mangalore, Karnataka, India

Date of Submission19-Nov-2019
Date of Decision07-Jun-2020
Date of Acceptance06-Aug-2020
Date of Web Publication8-Oct-2020

Correspondence Address:
Dr. Umesh Yeshwanth Pai
Department of Prosthodontics, Manipal College of Dental Sciences, Manipal Academy of Higher Education, Mangalore - 575 001, Karnataka
Login to access the Email id

Source of Support: None, Conflict of Interest: None

DOI: 10.4103/jips.jips_443_19

Rights and Permissions

Aim: This study assessed the effect of postetch cleansing on the surface microstructure, surface topography, and microshear bond strength (μSBS) of lithium disilicate and the resin cement.
Setting and Design: In Vitro analytical study.
Materials and Methods: Fifteen discs (10 mm diameter and 2 mm thickness) were fabricated from highly translucent lithium disilicate IPS Emax 2 ceramic (Ivoclar Vivadent, Schaan, Liechtenstein). Four resin cement (RelyX Ultimate, 3M ESPE) cylinders (0.9 mm diameter and 4 mm high) were placed on each ceramic disc (total n = 60). The samples were divided into three groups based on the surface treatment of the ceramic discs (20 resin cement cylinders on 5 discs in each group). Group I (HF) (control) etched with 9.6% HF with no postetch cleansing, Group II (HFP) etched with 9.6% HF for 20 s followed by rinsing with water and postetching cleansing with 37% phosphoric acid, and Group III (HFPU) etched with 9.6% HF followed by active application of 37% phosphoric acid followed by postetch cleansing in ultrasonic bath for 5 min. μSBS of resin cement to ceramic surfaces was tested following a standard protocol. Surface roughness was evaluated using an atomic force microscope. Surface topography and elemental analysis were analyzed using SEM/EDX. Mode of failure was also assessed.
Statistical Analysis Used: The data were analysed using one way analysis of variance and post hoc tukeys test.
Results: The μSBS were found to be highest for Group III (HFPU), followed by Group II (HFP) followed by Group I (HF) and were statistically significant. There was a difference in the surface topography and surface microstructure between the three groups. Mode of failure was predominantly adhesive.
Conclusion: The μSBS, surface topography, and surface microstructure were found to be superior in the groups, in which postetch cleansing was done as compared to the control in which no postetch cleansing was done.

Keywords: Ceramic, hydrofluoric acid, lithium disilicate, phosphoric acid, ultrasonic cleansing

How to cite this article:
Agarwal N, Bansal S, Pai UY, Rodrigues SJ, Shetty TB, Saldanha SJ. Effect of post etching cleansing on surface microstructure, surface topography, and microshear bond strength of lithium disilicate. J Indian Prosthodont Soc 2020;20:363-70

How to cite this URL:
Agarwal N, Bansal S, Pai UY, Rodrigues SJ, Shetty TB, Saldanha SJ. Effect of post etching cleansing on surface microstructure, surface topography, and microshear bond strength of lithium disilicate. J Indian Prosthodont Soc [serial online] 2020 [cited 2021 Aug 3];20:363-70. Available from: https://www.j-ips.org/text.asp?2020/20/4/363/297544

  Introduction Top

Recent advances in all ceramic restorations have helped in achieving excellent esthetic results.[1],[2] All ceramic restorations have emerged as a viable alternative to metal ceramic restorations for anterior esthetic restorations. The long-term survival rate of these restorations is dependent on the adhesion between the ceramic material and tooth structure.[3]

The invent of simultaneous phosphoric acid etching of enamel and hydrofluoric acid (HF) etching of ceramics by Horn in 1983 provided a major breakthrough in adhesive dentistry.[4] The most effective method of treating the intaglio surface of ceramic restoration is etching with hydrofluoric acid followed by application of silane coupling agent.[5] Hydrofluoric acid causes preferential dissolution of glassy matrix[6] and helps in the formation of “honeycomb-like structures” which enhances the micromechanical retention.[7] Silanation increases the wettability and also forms a covalent bond with resin cement at one end and ceramic at the other.[8]

However, there are various disadvantages of HF. It is a highly toxic substance and diffuses in the cell and poses serious health hazards like tissue necrosis.[9] Newer glass ceramics have a very fine crystalline structure that gets no benefits from HF etching.[10] Furthermore, HF etching of glass ceramics can result in the formation of insoluble silica fluoride salts[9],[11] which precipitate on the surface of ceramics acting as a barrier for the resin penetration, thereby hampering adequate bonding. This, in turn, can affect the resin ceramic bond strength.[12],[13]

Removal of HF is, therefore, highly advantageous and many techniques have been proposed to remove them such as brushing the fitting surface of the restoration with a clean tooth-brush,[14] thoroughly rinsing with water,[8] immersing in an ultrasonic bath with distilled water or 95% alcohol for either 5 or 10 min,[15],[16] application of 37.5% phosphoric acid with gentle agitation using a microbrush for 1 min[16] (active application of phosphoric acid is better than passive application),[17] and combination of these techniques.[16]

These techniques might seem time-consuming because of added steps and equipment required to complete the bonding procedure. However, there exists no concurrence in the literature regarding the necessity of these techniques in the routine all ceramic bonding protocol. Therefore, the purpose of thisin vitro study was to assess the effect of postetching cleansing on the surface microstructure, surface topography, and microshear bond strength (μSBS) of lithium disilicate. The null hypothesis is that there will be no effect of postetching cleansing on the surface microstructure, surface topography, and μSBS of lithium disilicate.

  Materials and Methods Top

The study was approved by institutional ethical committee, Manipal college of dental sciences, Mangalore (Protocol ref no. 18023). A total of 60 resin cement cylinders (n = 60) on 15 lithium disilicate discs were tested in this study. The samples were divided into three groups based on the surface treatment of the ceramic discs (20 resin cement cylinders on 5 discs in each group).

Fifteen disc specimens with 10 mm diameter and 2 mm thickness were fabricated from highly translucent lithium disilicate IPS Emax 2 ceramic (Ivoclar Vivadent, Schaan, Liechtenstein).

The discs were divided into three groups randomly as follows:

Group I (HF) (Control): 9.6% HF (Porcelain Etch, Ultradent Products, Jordan) was applied with a microbrush for 20 s and rinsing was done with water for 30 s. No postetching cleansing was done.

Group II (HFP): 9.6% HF (Porcelain Etch, Ultradent Products, Jordan) was applied with a microbrush for 20 s and then rinsed with water for 30 s. Using a microbrush, the specimens were then cleaned with 37% phosphoric acid (3M ESPE Scotch Bond Multi-purpose Etchant, St. Paul, MN, USA) using a gentle brushing motion for 30 s followed by rinsing with water for 30 s.

Group III (HFPU): 9.6% HF (Porcelain Etch, Ultradent Products, Jordan) applied with a microbrush for 20 s and rinsed with water for 30 s. Using a microbrush, the specimens were then cleaned with 37% phosphoric acid (3M ESPE Scotch Bond Multi-purpose Etchant, St. Paul, MN, USA) using a gentle brushing motion for 30 s. Cleaning was completed by immersion of the samples in an ultrasonic bath for 5 min.

Scanning electron microscopy for surface microstructure analysis

Two discs from each group were chosen randomly for microstructure analysis. Samples were desiccated for 48 h (Dry Keeper Simulate Corp., Tokyo, Japan) and sputtering was carried out with a platinum layer of 10 nm (Polaron Equipment Ltd., Hertfordshire, England, UK). Following sputtering, a scanning electronic microscope (SEM-Zeiss EVO MA 25; Carl Zeiss, Jena, Germany) was used for surface analysis in all the three groups.

Scanning electron microscopy (SEM) was supplemented with energy-dispersive X-Ray spectroscopy (EDS) to analyze the elemental composition of the discs subjected to different surface treatments.

Atomic force microscopy for surface topography analysis

Two ceramic discs from each group were selected randomly for surface roughness measurement using an atomic force microscope (AFM) (Bruker USA). Specimens were tested under a noncontact mode utilizing an AFM cantilever with magneto-resistive sensors incorporated in its tip. The measurements were made on each surface-treated ceramic disc at three random locations using a standardized rectangular spot (50 μm × 50 μm). The average or arithmetic surface roughness (Ra), root mean square value roughness (Rq), and peak height/maximum roughness (highest value – Rmax or Z) of the ceramics were noted as numeric values in nanometers.

Sample preparation

Following surface treatments, a silane coat was applied (Silane; Ultradent Products, Jordan) to all the discs with a microbrush for 60 s and gently air-dried. After silane application, 2 coats of adhesive (Single Bond Universal Adhesive; 3M ESPE, St. Paul, MN, USA) were applied, gently agitated and dried with a stream for evaporation of the solvent. Then, according to manufacturer's instructions, the adhesive was light-cured for 10 s. Four tygon tubes (Angiocath BD, Cundinamarca, Colombia) with a diameter of 0.9 mm and a height of 4 mm were placed on each surface-treated disc (4 tygons per ceramic disc; total n = 60) at a distance of 5 mm from each other and loaded with resin cement (RelyX Ultimate, 3M ESPE St. Paul, MN, USA). The samples were light-cured for 40 s at an intensity of 1,200 mw/cm2 (Blue Dent Smart, BG Light, Bulgaria), according to the manufacturer's instructions. A sharp blade was used for the removal of the tygon tubes from the disc. This resulted with each ceramic disc having four resin cement cylinders [Figure 1].
Figure 1: Specimen fabrication with resin cement cylinders on lithium disilicate discs

Click here to view

After the sample preparation, thermocycling (MSCT-3, Marcelo Nucci– ME, São Carlos, SP, Brazil) was done to simulate aging in the oral environment. 3500 cycles were done at 5 degrees and 55 degrees with a dwell time of 5 min simulating an intraoral aging of approximately 1 year

Microshear bond strength test

For universal testing, a heat cure PMMA block (Coltene Heat cure Denture Material; Coltene Whaledent, Switzerland) of dimension 40 mm × 15 mm × 15 mm was constructed to stabilize the ceramic discs. This was then positioned in the universal testing machine (Instron, Instron Engineering Corporation, Massachusetts). A blade was positioned at an angle of 90° at the junction of the resin/ceramic interface [Figure 2]. A shear load was applied to each resin cement cylinder, at a crosshead speed of 0.5 mm/minutes, until specimen fractured.[18] The values were expressed in MPa.[19]
Figure 2: Microshear bond strength testing

Click here to view

Fractographic analysis

A compound zoom microscope (CH 20I, Olympus, Olympus scientific Solutions America Corp) was used at ×40 magnification to classify the failure mode as adhesive (at the resin cement/ceramic interface, including pretesting failure), cohesive (within the resin cement or within the ceramic), or mixed (with both adhesive and cohesive failures).

Statistical analysis of the results for the μSBS values was performed by one-way analysis of variance and post hoc Tukey's test. A 95% confidence interval was used for all the statistical tests (α = 0.001). The statistical analysis was done with SPSS software (Version 15.0, SPSS Inc., Chicago, IL, USA).

  Results Top

Microshear bond strength test and fractographic analysis

The μSBS values (mean and standard deviation) and a statistical comparison of the different groups are shown in [Table 1] and [Table 2], respectively. μSBS values were significantly higher in Group III (HFPU) (58.88 ± 2.5 MPa) when compared with Group II (HFP) (49.52 ± 2.23 MPa) and Group I (HF) (42.11 ± 1.41 MPa) (P < 0.001) [Figure 3]. During μSBS measurements, there were 5, 1, and 2 pretesting failures in the groups HF, HFP, and HFPU, respectively. Fractographic analysis showed that adhesive failures were predominant in all the three groups (Group HF – 70%, Group HFP – 70%, and Group HFPU –85%) as seen in [Figure 4].
Table 1: Different letter (A/B/C) shows that there is statistical significant difference between the groups (P<0.001)

Click here to view
Table 2: Post Hoc Tukey Test showing significant difference between different groups

Click here to view
Figure 3: Bar diagram showing fractographic analysis

Click here to view
Figure 4: Bar diagram showing mean microshear bond strength values

Click here to view

SEM analysis

The results of SEM analysis at ×1000 and ×3000 magnification are demonstrated in [Figure 5] and [Figure 6], respectively. Group HF showed needle-like structures with vitreous islands. Microsurface of Group HFP showed lesser vitreous islands and increased density of needle-like structures, giving a dry earth appearance suggestive of increased roughness. Group HFPU showed a uniform interlocked networks of needle-like structures suggestive of most dense etching pattern. From Group HF to Group HFPU, an increase in the density and the uniformity of etching pattern was noted.
Figure 5: SEM images obtained from each experimental group (×1000): (a) Group HF, (b) Group HFP, (c) Group HFPU

Click here to view
Figure 6: Scanning electronic microscope images obtained from each experimental group (×3000): (a) Group HF, (b) Group HFP, (c) Group HFPU

Click here to view

Energy-dispersive X-ray spectroscopy analysis

The elemental composition in weight percentage for all the groups is summarized in [Table 3]. Traces of fluorine were found in group HF (2.1%) and group HFP (1.2%), but no fluorine was found in the group HFPU suggestive of no silica fluoride salts in that group.
Table 3: Elemental composition (in weight %) of all the three groups

Click here to view

Atomic force microscope analysis

The AFM results are presented in [Table 4] and [Figure 7]. Group HFPU showed the highest value of surface roughness (Ra, Rq, and Rmax) as compared to other two groups.
Table 4: Roughness values of all groups at 50 μm where Ra - is mean arithmetic mean, Rq - square root mean and Rz - maximum peak value or roughness value

Click here to view
Figure 7: Atomic force microscope images of Group HF, Group HFP, HFPU

Click here to view

  Discussion Top

The study was conducted to compare the effect of postetching cleansing on surface microstructure, surface topography, and shear bond strength of lithium disilicate. The efficacy of bond strength was evaluated using μSBS test. The effect of different surface treatment on microstructure of lithium disilicate substrates was evaluated by SEM supplemented with EDS and AFM topographic analysis. The mode of failure was assessed using a compound microscope.

It is a well-known fact that adhesion is a key factor in strengthening of esthetic restorations.[17] The unique mechanical and physical properties of materials involved alongwith the optimal surface enhancement of the bonding substrates interact to form a strong bond between the restoration and the tooth.[20] The materials include the tooth structure, bonding agent, resin cement, and porcelain restoration. Hydrofluoric acid causes preferential dissolution of the glassy phase of ceramic and provides an ideal microstructure for bonding. On the other hand, silane coupling agent provides a chemical covalent hydrogen bond that is an essential factor in creating a sufficient resin bond to silica-based ceramics.[21] There is a development of good bond strength between the ceramic surface and the luting agent if the surface of the ceramic is clean and rough.[22],[23] Stretched crystals and superficial irregularities were observed when HF was used to treat the surface of lithium disilicate. According to Höland et al.,[24] elongated crystals of lithium disilicate form the main crystalline phase and lithium orthophosphate constitutes the second phase of glass ceramic. A glassy matrix surrounds both these phases. HF, thus, creating irregularities in the lithium disilicate crystals removes this glassy matrix and the second phase. The present study showed similar results.

According to Della Bona et al., there is an increase in the potential for bonding of the ceramic surface if the surface area available is more, which, in turn, depends on the surface cracks and irregularities formed on the intaglio surface of the ceramic.[25] In the present study, surface roughness was highest for HFPU group, signifying more surface area available for bonding and hence better bond strength as compared to other groups. Phosphoric acid acts as a neutralizer. The bond strength increases when active application of phosphoric acid is done as it aids in the removal of the precipitates formed after etching with HF.[23] This allows for a deeper penetration of the resin cement in the ceramic.

In the present study, it is seen that the ultrasonic group has the highest value of bond strength and surface roughness, signifying that the postetching residues were cleaned properly. Use of ultrasonic helps to eliminate the surface fluoride residues, thus allowing a proper etched surface and hence increased surface roughness. Group HFPU showed an increase in roughness of 11.5% and 3.5% over HF and HFP, respectively. This was confirmed with the AFM images that show the highest value of peak in the Group HFPU. SEM images also show more dense and uniform pattern in the Group HFPU when compared with the other two groups. Clinicians who do not have an ultrasonic bath may use 37% phosphoric acid for the same purpose in order to increase the bond strength.

SEM is a commonly used method to analyze the microstructure after different surface treatments.[20],[22] This was supplemented with EDX analysis to give the elemental composition. When an electron beam is bombarded, energy present in the X-ray emitted from the specimen is measured and it gives the elemental composition of the specimen. One of the limitations of EDX analysis is that it cannot detect the elements having concentration <1%[22] The EDX analysis detected the presence of Na, Si, Al, O, C, and F on the specimens. However, the elemental composition of fluorine varied and was minimum in the HFPU group, suggestive of proper removal of the precipitates in that group.

AFM analysis showed that the values of Ra (arithmetic roughness), Rv (maximum valley depth), and Rp (maximum peak height) were found to be highest for HFPU group, signifying that the surface roughness was maximum with the HFPU group; hence, it has the maximum surface area for bonding and hence the highest bond strength. Group HFPU showed an increase in bond strength of 28.48% and 15.89% over HF and HFP group, respectively.

Etching was done with 9.6% HF for 20 s. Several studies have shown that there is a negative effect on the flexural strength of a lithium disilicate material when the etching time is increased[26] Furthermore, there is no increase in the bond strength on increasing the concentration of HF.[25] For bonding of ceramic to the resin, universal adhesive was used. It consists of silane and a monomer 10-methacryloyloxydecyl dihydrogen phosphate that helps improve the bond strength between the two.[26]

The methodology used in the study was to evaluate μSBS values as ceramics are brittle in nature. Moreover, on being compared with the macrotests used, microshear testing needs only small area of bonding, resulting in the uniform distribution of stresses.[27]

The fracture mode in the present study was adhesive followed by mixed or cohesive, which is an advantage as no sectioning is needed for fabrication of sample for performing the microshear test.[27] Majority of the specimens showed adhesive type of failure in all the groups as the bond between the resin cement and the restoration was weaker than the cohesive bond between the resin cement particles and/or the ceramic particles. 10% of the samples in group HF and group HFP showed cohesive failure. Cohesive failure in the resin cement occurs due to the forces that are nonhomogeneously distributed and are developed due to the weak bond strength between the luting agent and the restoration. This cohesive failure, in turn, results in the weakened unsupported restoration under the masticatory or the occlusal forces.[28]

Thermocycling of all the samples was also performed to maintain the oral environment. Samples were thermocycled at 5°C and 55°C at 3500 cycles with a dwell time of 5 min resulting in aging of about a year.[29]

The results of the present study proved that the postetching cleansing affects the μSBS between the lithium disilicate and the resin cement and also affects the microstructure and the surface topography of the lithium disilicate. Hence, the null hypothesis was rejected.

Limitations of this study are that only one type of resin cement was used. Comparing between different cements could be interesting and a point of further research. Another limitation could be the preload failures before testing the samples. More studies can be done with addition of groups and materials in the future.

Clinical application

The clinical application of the study is that on following these simple postetching cleansing protocols with readily available materials in most clinical practices, the bond strength increases by almost 29%, which, in turn, will enhance the longevity of the bonded lithium disilicate restorations.

  Conclusion Top

Within the limitations of the present study, the following conclusions can be drawn:

  • Postetching cleansing significantly increases the bond strength between the resin cement and ceramic restoration
  • Cleaning with 37% phosphoric acid followed by ultrasonic cleansing for 5 min results in superior bond strength as compared to cleaning with only phosphoric acid or no cleaning at all.


We would like to thank Dr. Ritwik Basu, MIT, Manipal, Dr. Kishore, MCODS, Manipal, Dental Material Department and Dr. Srikant, Professor and HOD, Department of Oral Pathology, MCODS, Mangalore for their constant support in the fulfillment of this study.

Financial support and sponsorship


Conflicts of interest

There are no conflicts of interest.

  References Top

Canay S, Hersek N, Ertan A. Effect of different acid treatments on a porcelain surface. J Oral Rehabil 2001;28:95-101.  Back to cited text no. 1
Kumbuloglu O, Lassila LV, User A, Vallittu PK. Bonding of resin composite luting cements to zirconium oxide by two air-particle abrasion methods. Oper Dent 2006;31:248-55.  Back to cited text no. 2
Peumans M, Hikita K, De Munck J, Van Landuyt K, Poitevin A, Lambrechts P, et al. Effects of ceramic surface treatments on the bond strength of an adhesive luting agent to CAD-CAM ceramic. J Dent 2007;35:282-8.  Back to cited text no. 3
Horn HR. Porcelain laminate veneers bonded to etched enamel. Dent Clin North Am 1983;27:671-84.  Back to cited text no. 4
Filho AM, Vieira LC, Araújo E, Monteiro Júnior S. Effect of different ceramic surface treatments on resin microtensile bond strength. J Prosthodont 2004;13:28-35.  Back to cited text no. 5
Addison O, Marquis PM, Fleming GJ. The impact of hydrofluoric acid surface treatments on the performance of a porcelain laminate restorative material. Dent Mater 2007;23:461-8.  Back to cited text no. 6
Chen JH, Matsumura H, Atsuta M. Effect of different etching periods on the bond strength of a composite resin to a machinable porcelain. J Dent 1998;26:53-8.  Back to cited text no. 7
Roulet JF, Söderholm KJ, Longmate J. Effects of treatment and storage conditions on ceramic/composite bond strength. J Dent Res 1995;74:381-7.  Back to cited text no. 8
Fabianelli A, Pollington S, Papacchini F, Goracci C, Cantoro A, Ferrari M, et al. The effect of different surface treatments on bond strength between leucite reinforced feldspathic ceramic and composite resin. J Dent 2010;38:39-43.  Back to cited text no. 9
Valandro LF, Della Bona A, Antonio Bottino M, Neisser MP. The effect of ceramic surface treatment on bonding to densely sintered alumina ceramic. J Prosthet Dent 2005;93:253-9.  Back to cited text no. 10
Santos GC Jr., Santos MJ, Rizkalla AS. Adhesive cementation of etchable ceramic esthetic restorations. J Can Dent Assoc 2009;75:379-84.  Back to cited text no. 11
Blatz MB, Sadan A, Kern M. Resin-ceramic bonding: A review of the literature. J Prosthet Dent 2003;89:268-74.  Back to cited text no. 12
Szep S, Gerhardt T, Gockel HW, Ruppel M, Metzeltin D, Heidemann D.In vitro dentinal surface reaction of 9.5% buffered hydrofluoric acid in repair of ceramic restorations: A scanning electron microscopic investigation. J Prosthet Dent 2000;83:668-74.  Back to cited text no. 13
Bailey LF, Bennett RJ. DICOR surface treatments for enhanced bonding. J Dent Res 1988;67:925-31.  Back to cited text no. 14
Jones GE, Boksman L, McConnell RJ. Effect of etching technique on the clinical performance of porcelain veneers. Quintessence Dent Technol 1986;10:635-7.  Back to cited text no. 15
Magne P, Cascione D. Influence of post-etching cleaning and connecting porcelain on the microtensile bond strength of composite resin to feldspathic porcelain. J Prosthet Dent 2006;96:354-61.  Back to cited text no. 16
Furukawa K, Inai N, Tagami J. The effects of luting resin bond to dentin on the strength of dentin supported by indirect resin composite. Dent Mater 2002;18:136-42.  Back to cited text no. 17
Giraldo TC, Villada VR, Castillo MP, Gomes OM, Bittencourt BF, Dominguez JA. Active and passive application of the phosphoric acid on the bond strength of lithium disilicate. Braz Dent J 2016;27:90-4.  Back to cited text no. 18
Belli R, Guimarães JC, Filho AM, Vieira LC. Post etching cleaning and resin/ceramic bonding: Microtensile bond strength and EDX analysis. J Adhes Dent 2010;12:295-303.   Back to cited text no. 19
Brum R, Mazur R, Almeida J, Borges G, Caldas D. The influence of surface standardization of lithium disilicate glass ceramic on bond strength to a dual resin cement. Oper Dent 2011;36:478-85.   Back to cited text no. 20
Kalavacharla VK, Lawson NC, Ramp LC, Burgess JO. Influence of etching protocol and silane treatment with a universal adhesive on lithium disilicate bond strength. Oper Dent 2015;40:372-8.  Back to cited text no. 21
Ozcan M, Alkumru HN, Gemalmaz D. The effect of surface treatment on the shear bond strength of luting cement to a glass infiltrated alumina ceramic. Int J Prosthodont 2001;14:335-9.  Back to cited text no. 22
Borges GA, Sophr AM, de Goes MF, Sobrinho LC, Chan DC. Effect of etching and airborne particle abrasion on the microstructure of different dental ceramics. J Prosthet Dent 2003;89:479-88.   Back to cited text no. 23
Höland W, Schweiger M, Frank M, Rheinberger V. A comparison of the microstructure and properties of the IPS Empress 2 and the IPS Empress glass ceramics. J Biomed Mater Res 2000;53:297-303.  Back to cited text no. 24
Della Bona A, Shen C, Anusavice KJ. Work of adhesion of resin on treated lithia disilicate based ceramic. Dent Mater 2004;20:338-44.  Back to cited text no. 25
Zogheib LV, Bona AD, Kimpara ET, McCabe JF. Effect of hydrofluoric acid etching duration on the roughness and flexural strength of a lithium disilicate-based glass ceramic. Braz Dent J 2011;22:45-50.  Back to cited text no. 26
Tian T, Tsoi JK, Matinlinna JP, Burrow MF. Aspects of bonding between resin luting cements and glass ceramic materials. Dent Mater 2014;30:e147-62.  Back to cited text no. 27
Mörmann W, Wolf D, Ender A, Bindl A, Göhring T, Attin T. Effect of two self-adhesive cements on marginal adaptation and strength of esthetic ceramic CAD/CAM molar crowns. J Prosthodont 2009;18:403-10.  Back to cited text no. 28
Palmer DS, Barco MT, Billy EJ. Temperature extremes produced orally by hot and cold liquids. J Prosthet Dent 1992;67:325-7.  Back to cited text no. 29


  [Figure 1], [Figure 2], [Figure 3], [Figure 4], [Figure 5], [Figure 6], [Figure 7]

  [Table 1], [Table 2], [Table 3], [Table 4]


Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
Access Statistics
Email Alert *
Add to My List *
* Registration required (free)

  In this article
Materials and Me...
Article Figures
Article Tables

 Article Access Statistics
    PDF Downloaded180    
    Comments [Add]    

Recommend this journal